Glass-Surface Area to Solution-Volume Ratio and Its Implications to Accelerated Leach Testing

摘要

The value of glass surface area to solution volume ratio (SA/V) can strongly influence the leaching rate of PNL 76-68 glass. The leaching rate is largely governed by silicon solubility constraints. Silicic acid in solution reduced the elemental release of all glass components. No components are leached to depths greater than that of silicon. The presence of the reaction layer had no measurable effect on the rate of leaching. Accelerated leach testing is possible since PNL 76-68 glass leaching is solubility-controlled (except at very low SA/V values). A series of glasses leached with SA/V x time = constant will yield identical elemental release. (ERA citation 08:009334)