Comparison of Compression Properties and Swelling of Beryllium Irradiated at Various Temperatures

摘要

A beryllium cylinder irradiated in Experimental Breeder Reactor (EBR-II) for four years at 700 to 760 K to a neutron fluence of 8.13 x 10 exp 22 n/cm exp 2 (total) or 1 x 10 exp 22 n/cm exp 2 (E > 1 MeV) was cut into samples and tested. Yield strength and plastic strain was determined in compression tests at 300, 723, 823 K and after annealing at 1173 K for one hour. The immersion density and helium content were measured on samples. An equation for swelling was derived from the data by regression analysis. The microstructure showed agglomeration of helium in voids or bubbles at the grain boundaries. (ERA citation 08:055967)