Comparative Study of Test Methods for Bituminized and Other Low- and Medium-Level Solidified Waste Materials

摘要

Various aspects of the behaviour of bituminized or cemented simulated low- or medium-level radioactive waste in contact with water or salt solutions have been investigated. The solubility (approximately 0.5%) and the diffusion coefficient (approximately 5.10 exp -8 cm exp 2 /sec) determining transort of water in pure bitumen have been measured for Mexphalte 40/50 at room temperature. A weighing method has been used to study water uptake and swelling of bituminized sodium nitrate, sodium sulphate or cation-exchange resin. The swelling of samples in contact with water was in some cases very pronounced. In strong salt solutions the tendency to swell is much less. The particle size of the embedded waste material is an important parameter. Thermal pre-treatment of cation-exchange resin before bituminization does not seem to improve the quality of the final product. The interaction between bituminized-exchange resin and concrete barrier materials has been studied. Microbial degradation of bitumen and bituminized waste under aerobic conditions has been investigated. It is probably of minor importance as far as leaching is concerned. A method for measuring leaching from a plane surface of cemented waste has been developed. The method avoids the problem of cracks between the sample and the container. Leaching from cemented sodium nitrate or sulphate was investigated. Absorption of CO sub 2 from the atmosphere was found to have only minor effect on Cs- and Na-leaching but gave a pronounced decrease in Ca-leaching. The use of silica-fume as an additive to cemented sodium nitrate decreased the leach rate by a factor 4. (Atomindex citation 15:031463)