Corrosion of Zircaloy 2 in Anaerobic Synthetic Cement Pore Solution

摘要

Measurements have been made of the corrosion rates of Zircaloy 2 tubes in anaerobic synthetic cement pore solution of pH 12.0-13.8. The samples were tested in the as-received condition by the polarization resistance technique using a Tafal constant of 52 mV/decade and, for all pH values, corrosion rates of 3.10 exp -5 A/m exp 2 (0.03 mu m/yr) were determined. These corrosion currents are at the lower limit of the experimental detection range of the technique used. Some samples were then held at a low electrochemical potential, namely -1850 mV SCE, for several days but this treatment had only a minor effect on the behaviour of the Zircaloy: the value of corrosion rate was increased by a factor of 3 and the free potential was temporarily lowered but drifted towards more positive values after the applied potential was removed. Attempts were made to remove the passive film from the surface of the samples by electrochemical reduction. For practical, experimental reasons, this was not successful and, instead, the effect of removing the film by scratching the surface was investigated. At both the free potential and at applied cathodic potentials, an anodic current was detected immediately and the surface was scratched but, in all cases, the scratched area repassivated within a few seconds and the anodic corrosion current fell accordingly. Thus, it may be concluded that active corrosion of Zircaloy 2 in anaerobic concrete will not occur and, by comparison with measurements on steel, it is likely that the passive corrosion rates will be even lower in concrete than those measured in the synthetic pore solution. (Atomindex citation 16:074123)