Comparison of High Temperature Steam Oxidation Behavior of Zircaloy-4 Versus Austenitic and Ferritic Steels under Light Water Reactor Safety Aspects

摘要

A comparative study of the oxidation behavior of Zy-4 versus steel No. 1.4914 and steel No. 1.4970 was performed in high temperature steam. Reactor typical tube sections of all three materials were exposed on both sides to superheated steam at temperatures ranging from 600 to 1300 sup 0 C for up to 6 h. The specimens were evaluated by gravimetry, metallography, and other methods. The results are presented in terms of weight gain, corresponding metal (wall) penetration and consumption as function of time and temperature. Concerning the corrosion resistance the ranking position of Zy-4 was between the austenitic and the ferritic steel. Because of the chosen wall dimensions Zy-4 and the austenitic steel behaved similarly in that the faster oxidation of the thicker Zy-4 cladding consumed the total wall thickness in a time equivalent to the slower oxidation of the thinner austenitic steel cladding. The ferritic steel cladding however was faster consumed because of the lower oxidation resistance and the thinner wall thickness compared to the austenitic steel. So besides oxide scale formation, oxygen diffusion into the bulk of the metal forming various oxygen-containing phases were evaluated - also in respect to their influence on mechanical cladding properties and the dimensional changes. (ERA citation 11:022952)