Effect of Heat Treatment and Impurity Concentration on Some Mechanical Properties V-15Cr-5Ti Alloy

摘要

The effects of heat treatment and O, N, C, Si, and S impurity level on the yield strength, ductility, and fracture mode for specimens from four different heats of the V-15Cr-5Ti alloy are presented. The heat treatments for the alloy consisted of annealing as-rolled material for one hour at either 950, 1050, 1125, or 1200 sup 0 C. The total oxygen, nitrogen, and carbon impurity concentration ranged from 400 to 1200 wppm. The Si concentration ranged from 300 to 1050 wppm, and the S concentration ranged from 440 to 1100 wppm. The yield strength and ductility for the alloy, regardless of impurity concentration, exhibited minimum and maximum values, respectively, for the 1125 sup 0 C anneal. The primary mode of failure for the tensile specimens was transgranular fracture. (ERA citation 11:032164)