Crack closure and healing studies in WIPP (Waste Isolation Pilot Plant) salt using compressional wave velocity and attenuation measurements: Test methods and results

摘要

Compressional wave ultrasonic data were used to qualitatively assess the extent of crack closure during hydrostatic compression of damaged specimens of WIPP salt. Cracks were introduced during constant strain-rate triaxial tests at low confining pressure (0.5 MPa) as specimens were taken to either 0.5, 1.0, or 1.5 percent axial strain. For three specimens taken to 1.0 percent axial strain, the pressure was increased to 5, 10 or 15 MPa. For the remaining specimens, pressure was raised to 15 MPa. Waveforms for compressional waves traveling both parallel and perpendicular to the direction of maximum principal stress were measured in the undamaged state, during constant strain-rate tests, and then monitored as functions of time while the specimens were held at pressure. Both wave velocities and amplitudes increased over time at pressure, indicating that cracks closed and perhaps healed. The recovery of ultrasonic wave characteristics depended upon both pressure and damage level. The higher the pressure, the greater the velocity recovery; however, amplitude recovery showed no clear correlation with pressure. For both amplitudes and velocities, recoveries were greatest in the specimens with the least damage. 13 refs., 15 figs., 1 tab.