Quantification of tritium 'heels' and isotope exchange mechanisms in La-Ni-Al tritides

摘要

Formation of tritium heels in LANA (LaNi(sub 5-x)Al(sub x)) 0.30 (x=0.30) and 0.75 tritides was quantified; size of the heel is dependent on storage and processing conditions. Absorption-desorption cycling of the tritide beds mitigates formation of the tritium heel and can reduce its size. The higher pressure material LANA 0.30 showed slower heel formation than LANA 0.75; this allows more tritium to be removed at the maximum processing temperature. In plant application, LANA 0.30 beds are used as compressors; except during compressor operation, their aging will be very slow. Tritium heel removal by D exchange was demonstrated. Absorption-desorption cycling during an exchange cycle does not improve the exchange efficiency. Residual tritium can be removed to very low levels. For a tritide bed scheduled for removal from the process, a final tritium level can be estimated based on the number of D exchange cycles. 13 refs, 8 figs, 6 tabs.