High Temperature Degradation of 5250-4 Polymer Resin

机译:5250-4聚合物树脂的高温降解

获取原文

摘要

5250-4 bismaleimide resin is used in high performance polymer matrix composites with high temperature aeronautical applications. This thesis investigated the thermal and oxidative degradation of 5250-4 neat resin powder in argon, air, and oxygen environments. The powder was aged at 163 deg. C, 177 deg. C, and 190 deg. C in all environments for at least 250 hours. Isothermal thermo-gravimetric analysis demonstrated that weight loss was negligible for aging in the argon environment, indicating weight loss is the result of an oxidative process at these temperatures. The 5250-4 powder exhibited an initial period of weight gain before eventually losing weight in both air and oxygen. The applicability of a closed loop oxidation scheme to 5250-4 gravimetric behavior was investigated. Kinetic parameters for the scheme were determined for the Air Force Research Laboratory's polymer matrix composite lifetime prediction modeling efforts.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号