Effect of Architecture of Acrylic Poly-Electrolytes on Inhibition of OxalateCrystallization

机译:丙烯酸聚电解质结构对草酸盐结晶抑制作用的研究

获取原文

摘要

A series of acidic acrylate polymers have been made by group transferpolymerization with narrowly defined molecular weight and structure. Both block and random copolymers with different proportions of carboxylate groups to butyl ester groups have been tested as inhibitors for the crystallization of calcium oxalate. The degree of inhibition is measured as the reduction in initial crystallization rate, determined by conductivity of the crystallizing solution. The inhibition increases with acid content of the polymer but is essentially unaffected by polymer architecture. These results are interpreted in terms of theories of polymer binding of solid surfaces. changing the butyl ester to a more hydrophilic ester also made little difference. Acrylates were much more effective than the equivalent methacrylates. Molecular modeling suggests that there was no difference in ion binding between these two faces of polycarboxylates. The higher inhibition efficiency is believed to arise from the closer chain packing on the crystal surface. jg.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号