Surface Mechanical Properties of Low-Molecular-Weight Polystyrene Below Its Glass-Transition Temperatures

摘要

Lap shear and friction force measurements were carried out on a series of monodisperse polystyrene (PS) films below the corresponding galss-transition temperatures. It showed that adhesion between the PS/PS interface was possible at the temperature below the bulk T_g, and the lower the molecular weight of PS, the lower the temperature at which the interfacial strength was detectable. The examination of a series of molecular weights indicated both the surface molecular motion and the magnitude of the interfacial strength were dependent on molecular weight and its distribution. And a steep increase of the friction force with increasing the test temperature was observed around 0 approx 30degC. The contact angle of water versus molecular weight measurements also showed a transition at room temperature. The behavior observed in this study was supposed to be due to the increased molecular mobility, and was in good agreement with the measured surface transiton temperatures by DSC.