A co-precipitation technique to prepare BaTa_2O_6

摘要

A mixture of ammonium oxalate and ammonium hydroxide was used to co-precipitate barium and tantalum ions as barium oxalate and tantalum hydroxide under basic conditions. On calcination at 750 deg C, this precursor yielded BaTa_2O_6 (BT) ceramics. This is much lower temperature as compared to that prepared by traditional solid-state method (1000 deg C) as reported for the formation of BaTa_2O_6. Transmission electron microscope (TEM) investigations revealed that the average particle size is 70 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 100.