Synthesis, growth, structural, optical, thermal and mechanical properties of an organic Urea maleic acid single crystals for nonlinear optical applications

摘要

A potential organic urea maleic acid (UMA) was synthesized and single crystals were grown at room temperature by slow evaporation and seed rotation methods. The grown crystal has been subjected to single crystal XRD analysis and found to have been crystallized in a noncentrosymmetric monoclinic crystal system with Cc as space group. The High resolution X-ray diffraction analysis revealed that the specimen is free from structural grain boundaries. The transparency of the grown crystal was confirmed by optical absorption and transmittance spectra with lower cut-off wavelength of 285 nm. The micro hardness test was carried out on different planes to study the load dependent hardness values. The dislocation density of the UMA crystal was estimated from the etching studies. The dielectric permittivity and dielectric loss of the grown crystal was carried out as a function of frequency for different temperatures along three crystallographic axes. Thermal properties of UMA crystals were studied by TG-DTA analysis and it is stable upto 112 degrees C. The laser induced surface damage threshold of the grown crystal was measured using Nd: YAG laser. The birefringence of the crystal measured in the visible region was found to vary with the wavelength. The particle size dependent SHG of the sample was measured with different input energies by Kurtz's powder method using Nd:YAG laser. (C) 2016 Elsevier Ltd. All rights reserved.