The synergistic effects of CO2 laser treatment with calcium silicate cement of antibacterial, osteogenesis and cementogenesis efficacy

摘要

Calcium silicate-based material (CS) has been successfully used in dental clinical applications. Some researches show that the antibacterial effects of CO2 laser irradiation are highly efficient when bacteria are embedded in biofilm, due to a photo-thermal mechanism. The purpose of this study was to confirm the effects of CO2 laser irradiation on CS, with regard to both material characterization and human periodontal ligament cell (hPDLs) viability. CS was irradiated with a dental CO2 laser using directly mounted fiber optics in wound healing mode with a spot area of 0.25 cm(2), and then stored in an incubator at 100% relative humidity and 37 degrees C for 1 d to set. The hPDLs cultured on CS were analyzed, along with their proliferation and odontogenic differentiation behaviors. The results indicate that the CO2 laser irradiation increased the amount of Ca and Si ions released from the CS, and regulated cell behavior. CO2 laser-irradiated CS promoted cementogenic differentiation of hPDLs, with the increased formation of mineralized nodules on the substrate's surface. It also up-regulated the protein expression of multiple markers of cementogenic and the expression of cementum attachment protein. The current study provides new and important data about the effects of CO2 laser irradiation on CS. Taking cell functions into account, the Si concentration released from CS with laser irradiated may be lower than a critical value, and this information could lead to the development of new regenerative therapies for dentin and periodontal tissue.