Solution and Aging of MAR-M246 Nickel-Based Superalloy

摘要

Solution and aging heat-treatments play a key role for the application of the superalloys. The aim of this work is to evaluate the microstructure of the MAR-M246 nickel-based superalloy solutioned at 1200 and 1250 A degrees C for 330 min and aged at 780, 880 and 980 A degrees C for 5, 20 and 80 h. The gamma' solvus, solidus and liquidus temperatures were calculated with the aid of the JMatPro software (Ni database). The as-cast and heat-treated samples were characterized by SEM/EDS and SEM-FEG. The gamma' size precipitated in the aged samples was measured and compared with JMatPro simulations. The results have shown that the sample solutioned at 1250 A degrees C for 330 min showed a very homogeneous gamma matrix with carbides and cubic gamma' precipitates uniformly distributed. The mean gamma' size of aged samples at 780 and 880 A degrees C for 5, 20 and 80 h did not present significant differences when compared to the solutioned sample. However, a significant increasing in the gamma' particles was observed at 980 A degrees C, evidenced by the large mean size of these particles after 80 h of aging heat-treatment.