Isothermal Transformation of a Commercial Super-Bainitic Steel: Part I Microstructural Characterization and Hardness

摘要

The effects of isothermal treatment on the microstructure and hardness of commercial super-bainitic steel were investigated. A series of isothermal treatments were carried out at temperatures of 210-250 A degrees C for different time periods. The results indicate that the bainitic reaction and hardness were very sensitive to the isothermal transformation temperature. The fine super-bainitic microstructure, containing the carbide-free bainitic ferrite lath and the carbon-enriched retained austenite film, can be produced by heating to 210 A degrees C for 30 h, resulting in a hardness of 662 HV. By increasing the isothermal transformation temperature, the bainitic transformation kinetic is accelerated; however, this is at the expense of coarsening bainitic ferrite laths and decreasing the bainitic ferrite quantity. The relationship between hardness and microstructures obtained under different isothermal treatments, which is correlated with the carbon concentration, dislocation density, bainitic amount and super-bainite size, is discussed in detail.