Effect of sintering condition and low-temperature degradation on the flexural strength and phase transformation of zirconia

摘要

? 2021 Editorial Council for the Journal of Prosthetic DentistryStatement of problem: The traditional sintering of zirconia takes an extended time, and accelerated treatments have been developed to reduce treatment time and manufacturing costs. Studies evaluating the effect of sintering time on the mechanical properties of zirconia are lacking. Purpose: The purpose of this in vitro study was to evaluate the effect of the sintering condition and the low-temperature degradation (LTD) of zirconia on the flexural strength of monolithic zirconia. Material and methods: Zirconia specimens (LUXEN Enamel) were sintered at 1500 °C, 1530 °C, and 1560 °C for 4, 5, 6, 7, and 12 hours and subjected to LTD (n=10). Control specimens were assessed in the nontreated condition. The 3-point flexural strength was measured by using a universal testing machine. The crystal phases of the specimens were compared and quantitatively analyzed through X-ray diffraction (XRD) analysis, and the crystal grain size was measured by using a field emission scanning electron microscope (FE-SEM). Two-way ANOVA and the independent sample t test were used to analyze the experimental results (α=.05). Results: In the group not subjected to LTD, there was no difference in flexural strength according to the change in sintering temperature and sintering time (P>.05). The group subjected to LTD showed a difference in flexural strength according to sintering time difference (P<.001). The flexural strength of the zirconia with LTD exposure increased compared with that of the zirconia specimen not subjected to LTD (P<.001). With LTD exposure, cubic and monoclinic crystals increased, tetragonal crystals decreased, and the particle size increased. As the sintering temperature increased, the particle size increased, but not according to the sintering time. Conclusions: At all sintering times, the flexural strength of zirconia was over 800 MPa, which is the minimum flexural strength of a 4-unit or longer prosthesis as specified in the International Organization for Standardization (ISO) 6872. With LTD exposure, the increase in the flexural strength of zirconia was associated with the phase change from tetragonal to monoclinic.