The fabrication of thermoelectric La_(0.95)Sr _(0.05)CoO_3 nanofibers and Seebeck coefficient measurement

摘要

The P-type perovskite oxides La_(1-x) SrxCoO_3 are a promising group of complex oxide thermoelectric (TE) materials. The thermoelectric properties of these oxides are expected to be significantly improved when their critical dimensions are reduced to the nanoscale. In this paper, the La_(0.95)Sr_(0.05)CoO_3 nanofibers, with diameters in the range of ～35 nm, were successfully prepared by the electrospinning process. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize these thermoelectric nanofibers. A micro-electromechanical (MEMS) tester was designed and fabricated to measure the Seebeck coefficient of the nanofibers. The measured voltage output was as large as 1.7 mV and the obtained Seebeck coefficient of the nanofibers reached 650 μV K~(-1).