BARIUM HEXAFERRITE THICK FILMS BY HOT PRESS SINTERING

摘要

BaFe12O19 ferrite thick films were screen-printed and sintered at 1150 degrees C under pressure (hot press sintering). The effects of the hot press sintering on the properties of barium hexaferrite thick films were investigated. The X-ray diffraction pattern shows improvement of the (001) texture under pressure. The porosity size of the hot press sintering samples decreases obviously and the surface compactness is improved as the pressure is increased. The films are quite anisotropic with magnetic easy axis perpendicular to the film plane. The largest remanence ratio achieved is 0.75 under the highest pressure of 4 MPa.