Production and properties of cordierite-based glass-ceramics from gold tailings

摘要

Cordierite-based glass-ceramics have been developed using gold tailings as one of the starting raw materials. The crystallization behaviour of gold tailings based glass samples was investigated by DTA, XRD, and SEM. On the basis of DTA analysis, nucleation experiments were carried out at 820 deg C for 2h and crystallization experiments were performed at 1010 deg C for 2h. X-ray diffraction analysis revealed that the major phase of the synthesized glass-ceramics was cofdierite along with a trace of iron cordierite. The properties of the synthesized cordierite-based glass-ceramics compared well with the values of industrial cordierite. Results indicate an interesting potential for gold tailings to produce useful materials.