Annealing effects on Czochralski grown Lu_(2)Si_(2)O_(7):Ce~(3+) crystals under different atmospheres

摘要

Cerium-doped lutetium pyrosilicate Lu_(2)Si_(2)O_(7):Ce~(3+) (LPS:Ce) single crystal samples grown via Czochralski method were annealed under air and H_(2) atmospheres from 350 to 1600 deg C. The x-ray excited luminescence spectra and UV as well as thermal stimulated luminescence spectra were measured. It was found that the luminescence efficiency after annealing in air at 1400 deg C was significantly enhanced compared to the unannealed samples. This phenomenon was suggested to be caused by the existence of some oxygen vacancies in the LPS:Ce crystals, and these oxygen vacancies can be effectively eliminated by means of annealing in air. Although the annealing will lead to the oxidization of cerium ions from Ce~(3+) ions to Ce~(4+), which is harmful to the luminescent efficiency, the annealing treatment does enhance the luminescent efficiency of LPS:Ce, without changing its luminescence mechanics.