首页> 外文期刊>Metalurgia >GROWTH OF THE CARBIDE LAYER DEPOSITED ON TE GRAIN BOUNDARIES DURING THE HYPERCARCURATION OF A LOW ALLOYED STEEL
【24h】

GROWTH OF THE CARBIDE LAYER DEPOSITED ON TE GRAIN BOUNDARIES DURING THE HYPERCARCURATION OF A LOW ALLOYED STEEL

机译:低合金钢超晶化过程中沉积在TE晶界上的碳化物层的生长

获取原文
获取原文并翻译 | 示例
获取外文期刊封面目录资料

摘要

Observations on the constituents morphology obtained by hypercarburation make possible a calculus of the growth kinetic (thickening) of the carbide film F, resulting a parabolic evolution in time (z chemical bounds K(c, #OMEGA#) centre dot sq root 2Dm centre dot t).Considering the intephasic interface structure the F carbide/matrix, the interface shift speed and the modification speed of this shape are calculated.Two parameters were introduced, R and #rho#, with 1/#rho# chemical bounds m+n/q+q/m, where m, n, p are the typical dimensions of the structural steps. R chemical bounds R(#rho#) modification speed of the shape on the volume and time units; #rho# chemical bounds shape factor.
机译:对通过高碳渗碳获得的成分形态的观察使得碳化物膜F的生长动力学(增稠)的演算成为可能,从而导致时间的抛物线演变(z化学界K(c,#OMEGA#)中心点平方根2Dm中心点t)。考虑到界面界面结构中的F碳化物/基体,计算了该形状的界面移动速度和改性速度,引入了两个参数R和#rho#,化学限为1 /#rho# + n / q + q / m,其中m,n,p是结构步骤的典型尺寸。 R的化学界R(#rho#)在体积和时间单位上的形状修饰速度; #rho#化学边界形状因子。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号