Strain rate and oxidation effects on crack initiation at 600 and 650 degrees C in a nickel-based superalloy

摘要

Nickel-based superalloys are sensitive to an oxidation-assisted intergranular crack (OAIC) growth mechanism. Crack initiation during slow strain rate tensile tests is investigated at 600 and 650 degrees C, at different strain rates, with or without oxidation on a direct-aged material. A V-shaped sample geometry is used to promote damage initiation for a specific stress triaxiality. The critical mechanical loading paths inducing intergranular crack initiation as well as the effect of oxidation are discussed.