Galvanic compatibility of corrosion protective coatings with AA7075 aluminum alloy

摘要

The galvanic compatibility of aerospace aluminum alloy AA7075 with cadmium (Cd), zinc (Zn), and zinc-cobalt-iron (Zn-Co-Fe, 32-37%Co and 1%Fe) alloys was investigated. A comparison of open circuit potential [OCP vs. saturated calomel electrode (SCE)] measurements in 0.6 mM NaCl showed that all coatings would act anodically to AA7075 with an exception of Zn-Co-Fe (37%Co + 1%Fe) alloy which was electropositive to AA7075. During the zero resistance ammetry (ZRA) measurement in 0.6MNaCl electrolyte the coupled OCP and current density were measured during 7 days of immersion and both Zn and Cd acted anodic and thus sacrificial to AA7075. Galvanic coupling of AA7075 with (37%Co + 1%Fe) Zn-Co-Fe alloy resulted in the consequent dissolution of the AA7075 aluminum alloy. In contrast, Zn-Co-Fe (32%Co + 1%Fe) alloy was found to be anodic to AA7075 during the first 26 h of immersion but after dezincification and cobalt enrichment at the surface became cathodic to the AA7075 aluminum alloy. During coupling with Zn, some pitting was also observed on AA7075.