Characterization of the insulator barrier and the superconducting transition temperature in GdBa2Cu3O7-delta/BaTiO3 bilayers for application in tunnel junctions

摘要

The optimization of the superconducting properties in a bottom electrode and the quality of an insulator barrier are the first steps in the development of superconductor/insulator/superconductor tunnel junctions. Here, we study the quality of a BaTiO3 tunnel barrier deposited on a 16 nm thick GdBa2Cu3O7-delta thin film by using conductive atomic force microscopy. We find that the tunnel current is systematically reduced (for equal applied voltage) by increasing the BaTiO3 barrier thickness between 1.6 and 4 nm. The BaTiO3 layers present an energy barrier of approximate to 1.2 eV and an attenuation length of 0.35-0.5 nm (depending on the applied voltage). The GdBa2Cu3O7-delta electrode is totally covered by a BaTiO3 thickness above 3 nm. The presence of ferroelectricity was verified by piezoresponse force microscopy for a 4 nm thick BaTiO3 top layer. The superconducting transition temperature of the bilayers is systematically suppressed by increasing the BaTiO3 thickness. This fact can be associated with stress at the interface and a reduction of the orthorhombicity of the GdBa2Cu3O7-delta. The reduction in the orthorhombicity is expected by considering the interface mismatch and it can also be affected by reduced oxygen stoichiometry (poor oxygen diffusion across the BaTiO3 barrier). (C) 2015 AIP Publishing LLC.