Short term online corrosion measurements in biomass fired boilers. Part 2: Investigation of the corrosion behavior of three selected superheater steels for two biomass fuels

摘要

The high temperature corrosion behavior of the boiler steels 13CrMo4-5 (1.7335), P91 (1.4903) and 1.4541 has been investigated during short-term test runs (-500 h) at a biomass fired grate furnace combined with a drop tube. For the test runs performed with 13CrMo4-5 and P91 chemically untreated wood chips have been used as fuel, whereas waste wood has been used for test runs with P91 and 1.4541. Online corrosion probes and a mass loss probe have been used applying a methodology developed in a previous study to correct for a measurement error occurring during short-term measurements with online corrosion probes (mass loss correction). Furthermore, deposit probe measurements have been performed to evaluate the deposit build-up rate and the chemical composition of deposits. SEM/EDX analyses of the corrosion probes have been performed subsequently to the test runs to gain information regarding the chemical composition and structure of the deposits as well as the corrosion layers.