The incorporation of cobalt into mesoporous molecular sieves MCM-41 and MCM-48 was carried out. Co-PO/MCM41 and Co-PO/MCM48 were prepared using Co(II) acetate solution adjusted to pH = 3.0 with phosphoric acid by the incipient wetness method. Photoacoustic spectroscopy (PAS) was used to study the local environments of Co(II) incorporated into mesopores. The band around 500 nm in PAS of as-prepared Co-PO/MCM41 and Co-PO/MCM48 with Co(II) acetate solution was changed to triplet bands around 600 nm. This could be assigned to the 4 A2(F)-> 4T1(P) transition of Co(II) surrounded tetrahedrally by oxygen ions after calcination. It may be attributable to that the octahedral cobalt species containing phosphate ligands in coordination sphere reacting with framework`s silanol groups to be dispersed atomically onto the surface of mesoporous molecular sieves as a tetrahedral species. This is unlike that the Co in Co-Cl/MCM41 and direct-synthesized Co-MCM41 transforms to Co oxide phase upon calcination. Co-PO/MCM41 and Co-PO/MCM48 were stable while treated with water.