Comparison between Oxygen and Nitrogen Plasma Treatment on Adhesion Properties and Antibacterial Activity of Metal Coated Polypropylene Fabrics

摘要

In this paper, an attempt was made to apply low temperature plasma treatment to improve the adhesion property of polypropylene fabrics. Oxygen and nitrogen plasmas were used for pre-functionalization of polypropylene fabrics. Then treated and untreated samples were coated with copper using direct current magnetron sputtering for 10 minutes. And the effect of oxygen and nitrogen pre-functionalization on adhesion properties between copper particles and polypropylene surface were studied. The textile properties of treated and untreated samples were evaluated by different standard testing methods in terms of both physical and chemical performances. The morphology changes of fabrics after plasma treatment were characterized by scanning electron microscopy. Fourier transform infrared spectroscopy analyses revealed chemical surface modifications occurring after the plasma treatments. Experimental results of the adhesion properties and surface properties are presented for the metal coated-polypropylene samples before and after low pressure plasma treatment, and results are compared. The adhesion properties of the activated samples are determined by abrasion and rubbing tests. The antibacterial counting test was used for determination of antibacterial efficiency of both treated and untreated samples, and durability of antibacterial properties was compared. The adhesion improvement has been related to the formation of different functional groups and changes in the topology of the surface.