Influence of silica on shape memory effect and mechanical properties of polyurethane-silica hybrids

摘要

Polyurethane block copolymer (PU) was synthesized and was followed by a sol-gel reaction with tetraethoxysilane (TEOS) to prepare high performance polyurethane-silica hybrids with shape memory function. Their tensile and shape memory properties were compared as a function of TEOS content and PU hard segment content. A tensile test showed that the mechanical properties were largely influenced by TEOS content, and the maximum elongation-at-break as well as maximum breaking stress and modulus were obtained when TEOS at 10 wt% was used. Shape memory of hybrids was also obtained from a thermomechanical test, and showed good shape retention and shape recovery of more than 80% for all samples. Consequently, by silica hybridization, an improvement in the mechanical properties and shape recovery force of PU could be achieved without any decrease in their shape recovery effect. (C) 2004 Elsevier Ltd. All rights reserved.