Separator grafted with siloxane by electron beam irradiation for lithium secondary batteries

摘要

Polyethylene (PE) separator grafted with 2,4,6,8-tetramethyl-2,4,6,8-tetravinylcyclotetrasiloxane (siloxane) was newly prepared by electron beam irradiation. The degree of grafting and morphology of the grafted separators were characterized by FT-IR and scanning electron microscopy (SEM). The polymer electrolytes based on the grafted separators were prepared by immersing the separators in the electrolyte containing 1 M LiPF{sub}6 in EC/DMC (1:1 by volume). The ionic conductivity of the grafted separators was changed with the degree of grafting and showed the highest value of 7 × 10{sup}(-4)S cm{sup}(-1) at the degree of grafting of 6%. The electrochemical stability limit of the grafted separator with the degree of grafting of 6% was increased to 5.2 V. The Li ion cell using the grafted separator also showed an improved performance, suggesting that the grafted separator is a good candidate for the separator of lithium batteries at high voltage operation.