The mechanical properties of an aqueous developed, chemically amplified; polynorbornene-based permanent dielectric have been investigated. The previously reported hexafluoroisopropanol norbornene and tert-butyl ester norbornene copolymer has been modified via two routes to improve the mechanical properties of the polymer and enable thick-film deposition. First, a third monomer, butyl norbornene (ButylNB) was added to the polymer backbone: The inclusion of 24 mol% ButylNB lowered the elastic modulus from 2.64 to 2.35 GPa and raised the dielectric constant from 2.78 to 3.48. The second approach added a low molecular weight, plasticizing additive in the copolymer formulation. Many additives were immiscible with the resin or did not affect the mechanical properties. Trimethyololproparte ethoxylate (TMPEO) was found to be a miscible additive that improved mechanical properties and could participate in crosslinking the final dielectric material. TMPEO interacted with the PAG, lowering its decomposition temperature. An optimal-formulation and processing scheme were determined. A formulation with 10 pphr TMPEO was measured to have a dielectric constant of 2.94, an elastic modulus of 1.95 GPa, a sensitivity at 365 nm of 175 mJ/cm(2), and a contrast of 4.36. (C) The Author(s) 2014. Published by ECS. All rights reserved.
展开▼