The effect of rare-earth oxides on the energy storage performances in BaTiO3 based ceramics

摘要

? 2022 Elsevier Ltd and Techna Group S.r.l.In this work, 0.7BaTiO3-0.3Sr0.2Bi0.7TiO3 (0.7BT-0.3SBT) ceramics with 0.15 mol various rare-earth oxides doped are designed and synthesized by the conventional solid-state route. All prepared samples exhibited a single perovskite phase and dense microstructure with fine grain size (0.2–0.5 μm) after sintering at 1180 °C. Especially, the Gd-doped 0.7BT-0.3SBT ceramics exhibited excellent energy storage performances; the corresponding recoverable energy density and efficiency were 3.2 J/cm3 and 91.5 under an electric field of 330 kV/cm, respectively. Meanwhile, doping with Gd caused the BT-based ceramics to possess excellent temperature (30–150 °C) and outstanding frequency stabilities (10–1000 Hz). Moreover, the pulsed charge-discharge experiments revealed that a high power density of 59 MW/cm3 and a fast discharge speed of 110 ns with outstanding temperature stability could be synchronously obtained in the Gd-doped composition. All these features are attractive for pulsed power applications.