Structure and diffusion characterization of SBA-15 materials

摘要

In situ formation of the micro- and mesoporous structures of SBA-15 materials was investigated. It was found that the structure is significantly different from that for cylindrical or hexagonal pores, which suggests that the SBA-15 is more complex than an array of hexagonally ordered channels. Nitrogen adsorption isotherms at 77 K provided evidence that large (primary) mesopores are accompanied by a certain amount of significantly smaller pores with a broad distribution in the micropore/small-mesopore range within the mesoporous walls of main channels. It was found that the microporosity can be controlled by the time of heating as well as the synthesis temperature. The diffusion properties of n-heptane as a probe molecule in four selected SBA-15 samples with different micropore volumes were studied by the standard zero length column technique and related to their structural characteristics. The results have shown that the diffusion process involving n-heptane at a low concentration level takes place inside the walls of main mesoporous channels and depends on the relative content of micropores. In the samples that have a relatively high content of micropores, n-heptane diffusivities are relatively low, their activation energies are high, and the process is similar to diffusion in typical microporous adsorbents, like zeolites. As the micropore content is decreased, diffusion becomes more and more controlled by secondary mesopores of the intrawall pore structure, rendering diffusion faster and activation energies lower.