The aim of the present investigation is to characterise cyclic deformation behaviour and plasticity-induced martensite formation of metastable austenitic stainless steels at ambient and elevated temperatures, taking into account the influence of the alloying elements titanium and niobium. Titanium and niobium are ferrite-stabilising elements which influence the ferrite crystallisation. Furthermore, they form carbides and/or carbonitrides and thus limit the austenite-stabilising effect of carbon and nitrogen. Several specimen batches of titanium and niobium alloyed austenite and of a pure Cr-Ni-steel for comparison were tested under stress and total strain control at a frequency of 5 Hz and triangular load-time waveforms. Stress-strain-hysteresis and temperature measurements were used at ambient temperature to characterise cyclic deformation behaviour. Plasticity-induced martensite content was detected with non-destructive magnetic measuring techniques. The experiments yield characteristic cyclic deformation curves and corresponding magnetic signals according to the actual fatigue state and the amount of martensite. Fatigue behaviour of X6CrNiTi1810 (AISI 321), X10CrNiCb189 (AISI 348) and X5CrNi1810 (AISI 304) is characterised by cyclic hardening and softening effects which are strongly influenced by specific loading conditions. Martensite formation varies with the composition loading conditions, temperature and number of cycles.
展开▼