Oxidation behaviour of Mo-Si-B-(Al, Ce) ultrafine-eutectic dendrite composites in the temperature range of 500-700 °C

摘要

A comparative study has been carried out to investigate the effects of Al and/or Ce additions on microstructure of Mo-Si-B alloys and their isothermal oxidation behaviour at 500 and 700 °C in laboratory air for 24 h. Microstructure of arc melted Mo-Si-B-(Al, Ce) alloys consists of bcc α-Mo dendrites embedded in ultrafine lamellar Mo_3Si and Mo_5SiB_2 eutectic matrix. Isothermal oxidation kinetics of ultrafine structured Mo-Si-B alloy at 500 °C has been found to show hardly any mass change during 24 h exposure. Addition of Al to Mo-Si-B alloy refines the microstructure, decreases the net mass loss at 700 °C by ～43%, whereas Ce does not bring about any significant change. The enhanced oxidation resistance of Mo-Si-B-Al alloy is due to the formation of Al-O rich inter-layer at the alloy/oxide interface along with the formation of a protective and dense Al_2(MoO_4)_3 outer layer, which reduces the sublimation of MoO_3 at 700 °C. Various transient/complex oxides formed on the alloys during their high temperature exposure have been examined to determine the oxidation mechanisms.