Preparation and properties of phenolic resin-based activated carbon spheres with controlled pore size distribution

摘要

Three kinds of phenolic resin-based activated carbon spheres (P-ACS) with different pore size distribution were prepared successfully by adding pore-forming agents to novolac-type phenolic resin. Polyethylene glycol and polyvinyl butyral, serving as pore-forming agents, evaporated during pyrolysis and left a small amount of carbon residue in the matrix of the phenolic resin-based carbon, thus changing the carbonization and activation behavior of the resin. Mesopores between 3 and 5 nm were created in the P-ACS, which possessed excellent adsorption properties for creatinine. Ferrocene has little effect on the carbonization process of the phenolic resin, but has a great impact on the activation process. Mesopores and macropores with a range form 3-5 to 10-90 nm were produced in the P-ACS, which exhibited large adsorption properties for VB_12, a larger molecule that creatinine. P-ACS without pore-forming agents exhibited a small specific surface area and mainly micropores, which resulted in a very small amount of creatinine and VB_12 adsorbed.