Disposition of fracture zones under hydrogen embrittlement

摘要

AbstractDisposition of the fracture zones during hydrogen embrittlement is discussed by using experimental data on crack growth kinetics by stress corrosion cracking and internal hydrogen embrittlement of the titanium alloy Ti‐7 AL‐2 Zr‐1,5 Mo‐1 V. The situation of these zones ahead of the crack tip depends on the kind of embrittlement and on KIand can change within wide