Fabrication and characterization of magnetic cobalt ferrite/ polyacrylonitrile and cobalt ferrite/carbon nanofibers by electrospinning

摘要

An electrospinning process was used to fabricate cobalt ferrite (CoFe2O4)-embedded polyacrylonitrile (PAN) nanofibers. Oleic acid-modified CoFe2O4 nanoparticles were dispersed in the PAN before spinning. The surface morphologies and structures of the nanofibers were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). SEM and TEM observation showed that the average diameter of the CoFe2O4/PAN nanofibers was 110 nm, and the magnetic CoFe2O4 nanoparticles were embedded in the PAN nanofibers. X-ray photoelectron spectroscopy was used to characterize the CoFe2O4/PAN and CoFe2CVcarbon nanofibers. Fiber magnetic properties were measured by vibrating sample magnetometry, showing that the saturation magnetization of the CoFe2O4/PAN nanofibers was 45 emu/g and that the fibers demonstrated superparamagnetic behavior.