Mesoporous LaFeO3: Synergistic Effect of Adsorption and Visible Light Photo-Fenton Processes for Phenol Removal from Refinery Wastewater

摘要

Mesoporous LaFeO3 as a visible light-driven photocatalyst was prepared by a nanocasting method using mesoporous silica (SBA-15) as a hard template. The as-prepared LaFeO3 photocatalyst was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N2 adsorption-desorption, X-ray photoelectron spectroscopy (XPS), and optical absorption spectra. The characterization studies and experimental results showed that LaFeO3 with porous structure caused by the removal of SBA-15 hard template could enhance the specific surface area of the resulting photocatalyst, which improves the phenol adsorption ability of the photocatalyst and in turn enhances its photo-Fenton catalytic activity. The photo-Fenton catalytic activity of the photocatalyst was investigated by photo-Fenton degradation of aqueous phenol under visible light irradiation. The effects of catalyst dosage, H2O2 concentration, and solution pH on the photo-Fenton catalytic degradation of phenol using mesoporous LaFeO3 were studied and optimized. Under the optimal conditions of 20 mg L~(-1) phenol, 1.0 g L~(-1) catalyst, and 10 mM H2O2 at pH = 5, the photo-Fenton degradation of phenol (93.47%) was achieved in 180 min under visible light irradiation. Furthermore, our results proved the stability and reusability of mesoporous LaFeO3 and revealed its catalytic mechanism for the photo-Fenton degradation of phenol.