Reinforcing effect of nanocrystalline cellulose and office waste paper fibers on mechanical and thermal properties of poly (lactic acid) composites

摘要

Nanocrystalline cellulose (NCC) was prepared from office waste paper (OWP) by sulfuric acid hydrolysis method in this paper and it was used to prepare a series of poly (lactic acid) PLA/NCC composites by using a dissolution method in solvent N, N-dimethylformamide solution. The results indicated that with the addition of only 3 wt% NCC, the composites exhibited outstanding mechanical property. The tensile, bending and impact properties of the PLA/3NCC composite were improved by 8.2%, 13.1%, and 35.9% than those of pure PLA, respectively. On this basis, office waste paper fibers (OWF) were also used as a physical blended filler to enhance PLA/NCC composites to reduce the preparation cost of PLA composites and the perfect PLA/NCC/OWF sample was easily manufactured by melting-blending and injection molding. According to the crystallization and melting performance table, both NCC and OWF can act as nucleating agent to promote the crystallization properties on composites, while the blends did not have positive effect on thermal stability. Furthermore, the water absorption and degradation properties of PLA composites were also studied. This work not only provided a novel idea for the utilization of office waste paper but also successfully produced environment friendly composites with favorable mechanical properties and crystallization performance.