Thermal Transition Behavior, Thermal Stability, and Flame Retardancy of Low-Melting-Temperature Copolyester: Comonomer Effect

摘要

Phosphorus-containing poly(ethylene terephthalate-co-diethylene terephthalate) (PEDT) with a low melting temperature was synthesized through esterification and copolycondensation of terephthalic acid, ethylene glycol, diethylene glycol (DEG), and 3-(hydroxyphenylphosphinyl)propionic acid (HPPPA). DSC results showed that PEDTs still were crystallizable and that the lowest melting temperature of the PEDTs was reduced to 118.0 °C although the chain regularity was destroyed by the incorporation of comonomers. It was found that the addition of HPPPA can improve the thermal oxidative stability of copolyesters. The results of the limiting oxygen index (LOI) test, the UL-94 vertical test, and the cone calorimeter test indicated that HPPPA endowed PEDT with good flame-retardant properties. The LOI values of the PEDTs were increased to 30.5-34.8, the UL-94 ratings of vertical burning were improved to V-0, and both the peak heat release rate (pHRR) and the total heat release (THR) obviously decreased.