Influence of Mass Ratio of Polyols on Properties of Polycaprolactone-Polyethylene Glycol/Methylene Diphenyl Diisocyanate/Diethylene Glycol Hydrogels

摘要

Polyurethane (PU) hydrogels with good hydrophilicity and biocompatibility have been applied as biomedical materials. A series of polyurethane prepolymers based on methylene diphenyl diisocyanate (MDI), polycaprolactone (PCL) and polyethylene glycol (PEG), using diethylene glycol (DEG) as the chain-extender, were synthesized; then the polyurethane hydrogels were obtained from the prepolymers using benzoyl peroxide (BPO) as a cross-linker by free radical polymerization. The influences of the ratio of polyols (PCL and PEG) on the contact angle, swelling ratio and morphology of the polyurethane hydrogel were investigated. The loading capacity and release behavior of chloramphenicol from the PCL-PEG/MDI/DEG hydrogels with different compositions were also studied. The contact angle and swelling degree results showed that the PCL-PEG/MDI/DEG hydrogel with PCL/PEG mass ratio of 3: 1 had higher hydrophilicity than that with PCL/PEG mass ratios of 1: 1 and 1: 3. All PCL-PEG/MDI/DEG hydrogels showed three dimensional porous structures; however, the pore size increased with increasing PEG content. The chloramphenicol release kinetics from PCL-PEG/MDI/DEG hydrogels indicated Fickian diffusion, and the drug release rate increased with increasing PEG content in the PU hydrogels.