Deterioration of concrete containing limestone powder exposed to sulfate attack at ambient temperature

摘要

This study investigates the deterioration of concrete containing limestone powder exposed to sulfate solution under ambient temperature (20 similar to 25 degrees C). Microstructure and mineral phases within the attacked concrete were measured by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). It was found that the addition of limestone powder increased the initial porosity of concrete. Consequently, a larger amount of SO42- ions diffused into the concrete containing limestone powder, and their degree of deterioration caused by sulfate attack increased with the increase in limestone powder content. At ambient temperature, gypsum and ettringite were the major attack products, respectively within the surface and near-surface portions of concrete containing limestone powder, which was consistent with the products of sulfate attack within concrete without limestone powder. Therefore, the type and distribution of the attack products in concrete had not been revised due to the addition of limestone powder. Nevertheless, the adverse influence of limestone powder on the sulfate resistance of concrete, even at ambient temperature, should be considered. Furthermore, effective measures should be implemented to improve the durability of concrete containing limestone powder in this environment.