Esterification of Cellulose Nanofibers with Valeric Acid and Hexanoic Acid

摘要

Cellulose nanofibers (CNFs) have received considerable attention as reinforcing fillers due to their excellent and versatile properties, including physical, morphological, and chemical features. Despite many advantages of CNFs, the hydrophilic nature of CNFs significantly limits their use as fillers. In this study, CNFs were modified by esterification with two kinds of carboxylic acids: valeric acid (VA) and hexanoic acid (HA). The degree of substitutions (DS) of VA-CNF and HA-CNF was 2.78 +/- 0.04 and 2.61 +/- 0.02, respectively. The dispersibility in an isopropanol solvent showed the controlled hydrophilicity of the modified CNFs. Moreover, the water contact angles of VA-CNF and HA-CNF were 79.2 +/- 3.1 degrees and 85.0 +/- 1.7 degrees, respectively, while the neat CNF was just 18.9 +/- 1.6 degrees. The thermogravimetric analysis (TGA) revealed that the modified CNFs have much better thermal stability than the neat CNFs. Also, the CNF films showed uniform-sized nano-porous structures after the modifications of CNFs. Combined with well-improved hydrophobicity, these multi-faceted results suggest that our esterification technique of CNFs can be applied in a wide range of eco-friendly materials applications.