Dual-responsive shape memory hydrogels with self-healing and dual-responsive swelling behaviors

摘要

Shape memory hydrogels (SMHs) can fix the hydrogels in a provisional shape and restore the initial shape under external stimulation. Herein, a dual-responsive shape memory hydrogel with dual-responsive swelling and self-healing properties is presented in this work. The SMHs were fabricated by one-step emulsion copolymerization of acrylic acid (AAc), acrylamide (AAm) and stearyl methacrylate (SMA). Sodium alginate (SA) was introduced as an interpenetrating polymer in the network. With ionic cross-linking between -COO- and Fe3+ or saline-reinforced hydrophobic association, the hydrogels can be fixed in a provisional shape, which can be restored by immersing the hydrogels in vitamin C solution or pure water, respectively. When the as-prepared hydrogels were immersed in FeCl3 solutions, additional ionic cross-linking between Fe3+ and -COO- could be formed, thus constructing the dual physically cross-linked (DPC) network, which endows the hydrogels with excellent fracture stress (2.6 MPa) and toughness (5.47 MJ/m(3)). Besides, the reversible physical cross-linkings endowed the hydrogel with outstanding self-healing capability. Furthermore, the pH and saline responsive swelling properties of the SMHs are additional fantastic properties. Therefore, we believe that this simple strategy provides a great opportunity for the preparation of SMHs with multiple intellectual performances.