Construction of physically crosslinked cellulose nanofibrils/alkali lignin/montmorillonoite/polyvinyl alcohol network hydrogel and its application in methylene blue removal

摘要

Herein, cellulose nanofibrils (CNF), alkali lignin (AL), and montmorillonite (MMT) were used to produce reinforced polyvinyl alcohol (PVA) hydrogels. The effects of MMT and AL contents on the rheological properties of reinforced hydrogel were studied. Compared with PVA/CNF hydrogel, the storage modulus of 40 wt% MMT-reinforced PVA hydrogel was increased by 41.4%. The rheological properties of MMT-enhanced PVA hydrogel could be adjusted by the variation of MMT loading. Also, as the PVA matrix had a synergistic effect with the embedded MMT and AL, the composite hydrogel demonstrated high efficiency in the removal of methylene blue dye (MB) from wastewater. Adsorption tests conducted at various time intervals (60-360 min) show that the hydrogels containing same content of MMT had higher removal efficiency. The MB adsorption of PVA/2CNF-0Li-40MMT was over 98.0%, whereas its adsorption equilibrium time and maximum adsorption capacity (q(m)) were 360 min and 67.2 mg/g, respectively. However, an extremely high content of MMT reduced the MB adsorption rate.