机译:高温下2D-C / SIC复合材料的抗压强度和损伤机制
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
Northwestern Polytech Univ Sci &
Technol Thermostruct Composite Mat Lab Xian 710072 Shaanxi Peoples R China;
2D-C/SiC composites; Compressive strength; Damage mechanism;
机译:高温下2D-C / SIC复合材料的抗压强度和损伤机制
机译:高温下面内剪切载荷下2D-C / SiC复合材料的破坏和强度
机译:通过低应力和高温蠕变强化2D-C / SIC复合材料
机译:低温下2D-C / SiC复合材料的动态压缩性能
机译:SiC / SiC陶瓷基复合材料损伤机制的多规模研究
机译:室温和高温下拉伸张力循环疲劳载荷下2 C / SiC和SiC / SiC陶瓷基复合材料损伤演化的比较
机译:低温下2D-C / SiC复合材料的动态压缩性能
机译:陶瓷材料的抗压强度和损伤机理。 I.氧化铝中压缩强度和损伤机理的温度 - 应变率依赖性。 II。弹塑性压痕过程中的阈值微裂缝