Structural, chemical and optical characterizations of an experimental SiO2-Y-TZP ceramic produced by the uniaxial/isostatic pressing technique

摘要

This study aimed to produce a new SiO2+Y-TZP ceramic via uniaxial/isostatic compression that was structurally and chemically characterized relating to its translucency and flexural strength. SiO2 and Y-TZP were mixed using a ball mill, pressed and sintered at 1150 degrees C. The optical and mechanical properties of the specimens were compared to lithium disilicate (LD) and zirconia-reinforced lithium silicate (ZLS) (Kruskal-Wallis, alpha = 0.05). The Fourier Transform Infrared Spectroscopy bands suggested an interaction between Si, O and Zr. Contrast ratio and translucency parameter of the experimental ceramic were higher and lower, (p = 0.000001) respectively, than those of the LD and ZLS. The experimental ceramic presented similar flexural strength to ZLS, but lower than LD (p < 0.0001). It can be concluded that this processing method is efficient to obtain a SiO2+Y-TZP ceramic and 1150 degrees C crystallizes SiO2 without inducing t-m transformation. The SiO2+Y-TZP ceramic presented lower translucency and higher masking ability than the commercially available glass-ceramics, but similar flexural strength to one glass-ceramics.