Effects of deformation rate on properties of Nd,Y-codoped CaF2 transparent ceramics

摘要

Different deformation rates of Nd,Y-codoped CaF2 transparent ceramics were prepared by ceramization of single crystals. The deformation rate effects on the crystallization behaviors, microstructures, mechanical properties, and optical performances were investigated for the first time. The results indicate that the comprehensive performances of Nd,Y-codoped CaF2 ceramic (Delta a = 62%) are the most optimal compared with other ceramics having different deformation rates (Delta a = 34%, 40%, 50%, and 75%). In further investigations of the optical properties, the Nd,Y-codoped CaF2 ceramic (Delta a = 62%) sample exhibited a high transparency (T-a 91%, 3-mm thick, 250 similar to 1200 nm), low light scattering, superior fracture toughness (K-1c similar to 0.71 MPa.m(1/2)), strong fluorescence emission, long lifetime (tau = 348.72 mu s), and broad FWHM (29.2 nm), promising a good candidate for high-power laser material.