Investigation of synthesized polymer on the rheological and filtration performance of water-based drilling fluid system

摘要

Based on the molecular structure requirement of the synthesized polymer resistant to higher temperature and the lower cost demand of water-based drilling fluid system, a kind of synthesized polymer Poly(SSS/AM/AMPS) was prepared by using 2-acrylamido-2-methylpropanesulfonic acid (AMPS), acrylamide (AM) and sodium p-styrenesulfonate (SSS) through inverse emulsion polymerization. Firstly, the molecular structure, molecular weight distribution and thermal stability were studied. Secondly, the Poly(SSS/AM/AMPS) was introduced into water-based drilling fluid system. As a result, when adding amount is 1.2 wt%, it was found that the water drilling fluids is more fitted to the Herschel-Bulkley flow model. Besides, before and after thermal aging test, the FLAPI of drilling fluid system is 9.20 and 9.40 mL, respectively. Moreover, it was shown that the higher temperature resistance of drilling fluid system was also improved, and the operation cost was decreased. Furthermore, the results of adsorption analysis, zeta potential method and morphology analysis shows that Poly(SSS/AM/AMPS) improves the filtration properties of drilling fluid system by absorption and physical plugging.